首頁 > 技術(shù)文章 > 1.1181化學(xué)成分

1.1181化學(xué)成分

點擊次數(shù):689更新時間:2022-03-07
Chemical composition % of steel C35E (1.1181): EN 10277-5-2008
Cr + Mo + Ni = 0.63
CSiMnNiPSCrMo
0.32 - 0.39max 0.40.5 - 0.8max 0.4max 0.03max 0.035max 0.4max 0.1

New opportunities for buyers!
Post free buying requirement of steel C35E (1.1181)


Mechanical properties of steel C35E (1.1181)

Nominal thickness (mm):to 1616 - 100100 - 250250 - 500500 - 1000






Rm - Tensile strength (MPa) (+N)550520500480470
Nominal thickness (mm):0.3 - 3


Rm - Tensile strength (MPa) (+A)540
Nominal thickness (mm):0.3 - 3


Rm - Tensile strength (MPa) (+CR)930
Nominal thickness (mm):5 - 1010 - 1616 - 4040 - 6363 - 100






Rm - Tensile strength (MPa) (+C)650-1000600-950580-880550-840520-800
Nominal thickness (mm):to 88 - 2020 - 5050 - 80





Rm - Tensile strength (MPa) (+QT)630600550500


Nominal thickness (mm):to 88 - 2020 - 5050 - 80





ReH - Minimum yield strength (MPa) (+QT)430380320290


Nominal thickness(mm):to 1616 - 100100 - 250




Re - Upper yield strength or
Rp0.2 - 0.2% proof strength (MPa) (+N)
300270245
Nominal thickness(mm):0.3 - 3


Rp0.2 0.2% proof strength (MPa) (+A)430
Nominal thickness(mm):to 100100 - 250250 - 500500 - 1000





Re - Upper yield strength (MPa) (+N)270245220210
Nominal thickness(mm):5 - 1010 - 1616 - 4040 - 6363 - 100






Rp0.2 0.2% proof strength (MPa) (+C)510420320300270




KV - Impact energy (J) (+QT)+20°
35


KV - Impact energy (J) (+N)+20°
27


KV - Impact energy (J) transverse, (+QT)+20°
22




A - Min. elongation at fracture (%) transverse, (+N)15
Nominal thickness (mm):5 - 1010 - 1616 - 4040 - 6363 - 100






A - Min. elongation at fracture (%) (+C)67899
Nominal thickness (mm):to 88 - 2020 - 5050 - 80





A - Min. elongation at fracture (%) longitud., (+QT)17192020


A - Min. elongation at fracture (%) longitud., (+N)21


A - Min. elongation at fracture (%) longitud., (+A)22


Nominal thickness (mm):to 1616 - 100100 - 250




A - Min. elongation Lo = 5,65 √ So (%) (+N)181919


Brinell hardness (HBW): (+SH)154 - 207
Brinell hardness (HBW): (+A)183
Vickers hardness ( HV): (+CR)275
Vickers hardness ( HV): (+A)170


Properties of steel C35E (1.1181)
Weldability: It can be welded quite well without any precautions.
Hardenability: Low hardenability; core quenching in water till a diameter of 12-15 mm; as far as bigger diameters are concerned, it hardens only till a certain depth, inversely proportional to diameter, like all nonalloy steels with medium-high carbon content.


Equivalent grades of steel C35E (1.1181)
Warning! Only for reference
EU
EN
USA
-
Germany
DIN,WNr
Japan
JIS
France
AFNOR
England
BS
Italy
UNI
Spain
UNE
China
GB
Sweden
SS
Finland
SFS
Russia
GOST
Inter
ISO
C35E
1035
Ck35
S35C
XC38
XC38H1
080M36
CFS6
C35
C35k
F1130
35
1572
C35
35
C35E4


地址:上海市松江區(qū)泗涇鎮(zhèn)泗磚公路600號松江鋼材城
© 2019 上海隆繼金屬集團(tuán)有限公司(ccbangtu.com) 版權(quán)所有 總訪問量:580333

備案號:滬ICP備12025537號-4 技術(shù)支持:化工儀器網(wǎng)

久久麻豆亚洲AV成人无码国产| 国产成人精品三级麻豆| 东京无码熟妇人妻av在线网址| 欧美av| 男人tv天堂精品一区二区| 免费人成视频x8x8入口app| 亚洲精品无码av久久久久久| 亚洲av夜夜欢一区二区三区| 国模精品一区二区三区| 亚洲国产精品成人麻豆| 无码国精品一区二区免费| 精品亚洲一区二区三区在线观看 | 综合久久| 亚洲精品尤物av在线观看任我爽| 久别的草原在线看视频免费| 国产手机在线精品| 久久国产加勒比精品无码| 久久国产欧美国日产综合抖音| 精品人妻久久久久久888| 国产在线拍揄自揄拍免费下载| 精品人妻人人做人人爽夜夜爽| 麻豆乱码国产一区二区三区| 玩弄chinese丰满人妻videos| 无码精品黑人一区二区三区| 日本少妇人妻xxxxx18| 综合亚洲日韩偷窥另类图片 | 午夜无码熟熟妇丰满人妻| 亚洲精品区无码欧美日韩| 久久人人做人人妻人人玩精品VA | 成人午夜亚洲精品无码网站| 日本免费无码一区二区到五区| 思思久久精品在热线热| 99久久亚洲精品日本无码| 少妇被粗大的猛烈进出a片久久久 韩国精品无码少妇在线观看 | 国产av一区二区三区最新精品| 一本加勒比hezyo无码人妻| 久久精品国产色蜜蜜麻豆| 久久人人爽人人爽人人AV东京热| 久久99国产精品久久99| 国产JJIZZ女人多水免费| 秋霞影院午夜伦A片欧美|